| Quantity(Kilograms) | 1 - 420 | >420 |
| Est. Time(days) | 3 | To be negotiated |
Due to the frequent traffic of loading and discharge of cargo, the truck container is easily damaged by the heavy impact, collision and wearing. The normal painting can decorate the truck bed rather than protect it effectively. The bed liner of a new truck is usually destroyed in less than 1 year after application. Spray polyurethane elastomer innovated a brand new solution for the truck bed liners protection. SWD truck bed liners special polyurethane coating is high flexible and wearing resistance performance. It has been widely applied in the automotive manufacturing industry in the US with perfect reputation.
Characteristics
It is high reactive and rapid curing and able to be sprayed forming on any bending surfaces. The coating film is dense tough and flexible, with high adhesive strength with substrate and excellent properties of impact resistance, anti-collision, wear resistance and slip resistance, stable anticorrosion performance endured acid, alkali, salt and other solvents. It performs well in high temperature variation and anti-aging and bears the alternative impact in wind, rain, frost and snow conditions.
Specifications
Adhesive strength (concrete base) 12.3Mpa
Tear strength 76kN/m
Tensile strength 18.3Mpa
Elongation 330%
Temperature variation -40------+120℃
Wear resistance (700g/500r) 4.3mg
Acid resistance (10%H2SO4 or 10%HCI, 30d) no rust no bubbles no peel
Alkali resistance 10%NaOH, 30d no rust no bubbles no peel
Salt resistance 30g/L, 30d no rust no bubbles no peel
Salt spray resistance 2000h no rust no bubbles no peel
Oil resistance 0# diesel crude oil 30d no rust no bubbles no peel
Data of performance
Color Multiple colors as customers’ need
Luster glazed
Density 1.02g/cm3
Volume solid content 99%±1%
VOC 0
Recommended dry film thickness 1000-2500μm
Theoretical coverage 2.04kg/sqm (calculated by the above solids percentage and dry film thickness of 2000 microns)
Practical coverage Allow appropriate loss rate
Dry time 5-20s
Overcoating interval min: 1h, max: 24h
Overcoating method Special polyurea equipment spray (imported or local support)
Flash point 200℃
Recommend procedures
No. | Name of products | Layers | Dry film thickness(μm) |
1 | SWD polyurea special primer | 1 | 50 |
2 | SWD truck bedliners special polyurethane coating | 1 | 1500 |
Total |
| 2 | 1550 |
Application scopes Wear resistant protection of bed liners of truck, pick-up truck and dumpers, car paint protective coatings.
grinder project application
1.We are factory.
SWD New Material (Shanghai) Co., Ltd is a professional manufacturer of polyurea polyurethane coating and pu foam in China, with headquarter in US for over 40 years. We have our own production workshops focusing on all aspects of anticorrosive waterproof, insulation fields. US technology and made in China, high quality and nice prices.
2.OEM is accepted ?
We have our own R&D team and specialists, so we can customize the product that customer’s require.
3.How to guarantee the high quality?
We have the ISO9001 quality management system certificate, we are PDA member and have standard test reports. We strictly implement the rules according to the quality standard in every aspects from the purchase of raw material to the production process and outgoing of products.