Polyurea is a type of compound reacted by isocyanate component (short to part A) and amide blend (short to part B). Following the high-solids coatings, waterborne coatings, radiation curable coatings, powder coatings and other pollution free coating technologies, Spray Polyurea Elastomer (referred SPUA) technology is a solvent-free, pollution-free green application coating advanced technology developed to meet environmental requirements in nearly two decades abroad. It’s a revolutionary leap of traditional construction technology which combines new technology new material and new procedures together. Its a breakthrough for changing the traditional anticorrosion protective concept and set up a higher standard for the industrial material protection industry.                                                                                 

Characteristics          

SWD two component solvent free environment friendly pure polyurea industrial coating is developed by SWD Urethane Co., USA in 1992. Based on the high reactivity and fast curing property, it can be sprayed forming at any bent, inclined and vertical surface without sagging. With super adhesive strength and impact resistance characteristics, the coating is flexible, impact resistant and seamless that able to completely insulate air and water and oxygen penetration. It integrated anticorrosion, waterproof, wear resistance, aging resistant performances, no pulverization and crack peel up or fall down after long- term outdoor work with alternating ambient conditions of cold, heat, rain and snow.                                                                                 

Specifications 

Adhesive strength (concrete base)                   2.9 Mpa( or substrate broken)

Adhesive strength (steel base)                      11.3 Mpa

Tear strength                                                      80.6kN/m

Tensile strength                                                17.8Mpa  

Elongation                                                          470%

Penetrate resistance                                       2.3Mpa

Temperature variation                                     -40------+120℃

Wear resistance  (700g/500r)                         5mg

Acid resistance (10%H2SO4 or 10%HCI, 30d)           no rust no bubbles no peel

Alkali resistance 10%NaOH, 30d                         no rust no bubbles no peel

Salt resistance 30g/L, 30d                                    no rust no bubbles no peel

Salt spray resistance 2000h                                 no rust no bubbles no peel

Oil resistance 0# diesel crude oil 30d                  no rust no bubbles no peel                                                                                

Data of performance

Color                                       Multiple colors as customers’ need

Luster                                     glazed 

Density                                  1.01g/cm3  

Volume solid content            99% ±1%

VOC                                           0

Recommended dry film thickness   1000-3000μm

Theoretical coverage             2.04kg/sqm (calculated by the above solids percentage and dry film thickness of 2000 microns)

Practical coverage                Allow appropriate loss rate

Dry time                                   5-20s

Overcoating interval              min: 1h, max: 24h

Overcoating method             Special polyurea equipment spray (imported or local support)

Flash point                               200℃                                                                                

Recommended procedures

Application scopes           Anticorrosion waterproof protection in the fields of  construction, chemical, traffic, metallurgy, power generation, aerospace, marine, shipping industries and etc.