SWD building external wall heat reflection coating

SWD building external wall heat reflection coating   

Descriptions                

 Heat is a necessary condition for human’s survival, but too much energy from sunshine and fuel becomes a pressure and burden. The accident and death toll caused from over temperature is innumerable every year in the world. Every summer, the energy consumption of air conditioning, fans and other cooling equipment occupied 30% of all the energy amount whole year which is a huge waste. The environment friendly building waterproof energy efficient cold coating developed by SWD Urethane Co., USA in 1990s can not only insulate heat and lower the building temperature, but also provide a waterproof protection layer for the building roof and wall surface. The service can reach more than 15 years and it has been widely applied in Europe and America.                                                                                

Characteristics             

 Applied with unique formula and scientific process, SWD8005 coating takes the one component environment friendly water base macromolecule prepolymer resin as main materials. The coating film is dense, with excellent sealing and penetration resistance performance and high adhesive strength with substrate. It has high reflection rate against sunlight and hemispherical emissivity that has super heat reflection which able to adjust the temperature more than 10℃. With high performance of waterproof, erosion resistance and stain resistance, it can bear long-term outdoor application with no peel off, pulverization and yellowing. It is green and environment friendly will do no harm during application.

Specifications

Status on the container                                  no blocks after mixing, uniform state

Application condition                                      brush is available

Appearance                                                        normal

Hading (white or light colora) (g / m2)              ≤ 150 

Dry time / h                                                 Tack free time≤2, solid dry≤24

Adhesive strength(grid method)/degree           ≤ 1 

Impact resistance / cm                                  ≥ 30

sunlight reflection rate                                    0.83

Hemispherical emissivity                                  0.89

Insulation temperature adjustment                   ≥10 ℃

Insulation temperature attenuation(white)         ≤12 ℃

Tensile strength                                               ≥1.2Mpa

Elongation                                                       ≥ 200%

Temperature variability (5 cycles):                 normal

Acid resistance c(5% H2 SO4)                      168h normal

Salt spray resistance                                     1000h no bubbles no peel 

Artificial weather resistance                            400h no bubbles, no peel off, no crack

(White or light colored a,d)                          pulverization ≤1; discolor≤2 grade 

Data of performance

Color                                   Multiple colors as customers’ need

Luster                                   glazed

Density                                1.12g/cm3

Volume solid content               81% ±2%

VOC                                      ≤10g/L

Recommended dry film thickness   150-200μm

Theoretical coverage             0.17kg/sqm (calculated by the above solids percentage and dry film thickness of 150 microns)

Practical coverage                Allow appropriate loss rate

Curing mechanism                room temperature cure

Tack free time                     1-3h

Overcoating interval              min: 3h, max: 25h

Overcoating method             Airless spray, Air spray, Brush, Roller

Flash point                            Non flammable non explosive, safety and environmental protection

Recommend procedures: 

Application scopes      

 Insulation protection of building roof, walls, industrial plant roof, storage tanks and other industrial equipment.